Coated article with improved barrier layer structure and method of making the same

ABSTRACT

A coated article, and a corresponding method of making the same are provided. The coated article includes a coating supported by a substrate, the coating including a thin metal or metal nitride contact layer (e.g., NiCr, Ni, Cr, CrN x  or NiCrN x ) located directly between and contacting an infrared (IR) reflecting layer (e.g., Ag) and an oxide barrier layer (e.g., NiCrO x ).

This application claims priority on Provisional U.S. patent applicationSer. No. 60/331,160, filed Nov. 9, 2001, the disclosure of which ishereby incorporated herein by reference.

TITLE OF THE INVENTION

This invention relates to a coated article including a metal or metalnitride layer provided between an IR reflecting layer (e.g., Ag layer)and an oxide barrier layer (e.g,. NiCrO_(x)), and a method of making thesame.

BACKGROUND OF THE INVENTION

Coated articles provided for solar control purposes are known in theart. For example, see U.S. Pat. No. 5,344,718, which discloses a layerstack of: glass/Si₃N₄/NiCr/Ag/NiCr/Si₃N₄. In coatings such as this, NiCrbarrier layers are commonly used to protect the Ag (silver) in low-Etype coatings.

Unfortunately, metallic NiCr is characterized by high absorption whichreduces transmittance of the final coated article. Due to this highabsorption problem, those in the art desiring products with high visibletransmission have been forced to use very thin NiCr barrier layers. Forexample, the NiCr layers in the aforesaid '718 patent are “less thanabout 7 Å” thick, in order to obtain the desired visible transmission.The thinner such layers are, the less barrier functionality andprotection they provide. Consequently, those skilled in the art havebeen seeking to increase barrier layer transmission by introducingoxygen and/or nitrogen to NiCr barrier layers (e.g., see U.S. Pat. No.6,014,872 at col. 4, lines 40-50).

Consider a layer stack of glass/Si₃N₄/NiCrO_(x)/Ag/NiCrO_(x)/Si₃N₄.While the NiCrO_(x) protective barrier layers are more transparent thanNiCr protective barrier layers, they have their problems. For instance,the use of NiCrO_(x) protective barrier layers contacting the Ag layeron respective sides thereof can sometimes lead to problems with respectto durability and/or heat treatability. It is believed that duringdeposition (e.g., via sputtering) of a coating including NiCrO_(x)protective barrier layers, the Ag layer is exposed to the oxygen plasma(and thus chemically active atomic oxygen in that plasma) used indepositing the NiCrO_(x); this is especially true with respect to thetop surface of the Ag layer when an upper NiCrO_(x) protective barrieris applied directly thereto. The exposure of the Ag to this oxygeninclusive plasma is believed to sometimes lead to Ag adhesion problems.

In view of the above, it will be apparent to those skilled in the artthat there exists a need for an improved barrier layer(s) structure forprotecting an IR reflecting layer (e.g., Ag).

BRIEF SUMMARY OF THE INVENTION

An object of this invention is to provide an improved barrier layer(s)structure for protecting an IR reflecting layer such as Ag in a coatedarticle, and a corresponding method of making the same.

Another object of this invention is to provide a barrier layer(s)structure which is capable of protecting an IR reflecting layer, andwhich is both fairly transmissive to visible light and enables a durablefinal coated article.

Another object of this invention is to fulfill one or more of the abovelisted objects and/or needs.

In certain example embodiments of this invention, one or more of theabove-listed objects and/or needs is/are fulfilled by providing a coatedarticle comprising: a glass substrate; a coating supported by the glasssubstrate, wherein the coating comprises a first dielectric layer, afirst NiCrO_(x) inclusive layer, an Ag inclusive layer, a secondNiCrO_(x) inclusive layer, and a second dielectric layer, wherein the Aginclusive layer is located between the first and second NiCrO_(x)inclusive layers; and wherein the coating further includes a metal ormetal nitride protective contact layer located between and contactingthe Ag layer and one of the NiCrO_(x) inclusive layers.

In other example embodiments of this invention, one or more of theabove-listed objects and/or needs is/are fulfilled by providing a coatedarticle including a coating supported by a substrate, the coatingcomprising: a NiCrO_(x) inclusive layer; an Ag inclusive layer; and ametal or metal nitride layer located between and contacting each of theNiCrO_(x) inclusive layer and the Ag inclusive layer.

In other example embodiments of this invention, one or more of theabove-listed objects and/or needs is/are fulfilled by providing a coatedarticle including a coating supported by a substrate, the coatingcomprising: an oxide layer including an oxide of a metal or metal alloy;a metallic infrared (IR) reflecting layer; a metal or metal nitrideprotective contact layer located between and contacting each of themetallic IR reflecting layer and the oxide layer; and wherein the metalor metal nitride contact layer comprises the same metal or metal alloyas is in the oxide layer.

In still further embodiments of this invention, one or more of theabove-listed objects and/or needs is/are fulfilled by providing a methodof making a coated article, the method comprising: providing a glasssubstrate; depositing a first dielectric layer so as to be supported bythe substrate; depositing an Ag layer on the substrate over the firstdielectric layer; depositing a metal or metal nitride contact layer onthe substrate directly over and in contact with the Ag layer; depositinga layer comprising NiCrO_(x) on the substrate directly over and incontact with the metal or metal nitride contact layer; and

depositing another dielectric layer on the substrate over the layercomprising NiCrO_(x).

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross sectional view of a coated article according to anembodiment of this invention.

FIG. 2 is a cross sectional view of a coated article according toanother embodiment of this invention.

FIG. 3 is a cross sectional view of a coated article according to yetanother embodiment of this invention.

DETAILED DESCRIPTION OF EXAMPLE EMBODIMENTS OF THE INVENTION

Referring now more particularly to the accompanying drawings in whichlike reference numerals indicate like parts throughout the severalviews.

Coated articles according to different embodiments of this invention maybe used in the context of architectural windows (e.g., IG units),automotive windows, or any other suitable application. Coated articlesherein may or may not be heat treated (e.g., thermally tempered, heatbent, or the like) in different embodiments of this invention.

FIG. 1 is a side cross sectional view of a coated article according toan embodiment of this invention. The coated article includes substrate 1(e.g., clear, green, bronze, or blue-green glass substrate from about1.0 to 10.0 mm thick, more preferably from about 1.8 mm to 4 mm thick),first dielectric layer 3, lower barrier layer 5, lower barrier contactlayer 7 (which contacts IR reflecting layer 9), first conductivemetallic infrared (IR) reflecting layer 9, upper barrier contact layer11 (which contacts IR reflecting layer 9), upper barrier layer 13, andupper dielectric layer 15. The “contact” layers 7 and 11 each contact IRreflecting layer 9. Example non-limiting materials for layers 3-15 areillustrated in FIG. 1. The aforesaid layers 3-15 make up a solar controlcoating (e.g., a low-E or low emissivity type coating) which may beprovided on glass or plastic substrates 1. The layer stack 3-15illustrated in FIG. 1 may, in certain alternative embodiments of thisinvention, be repeated on substrate 1 one or more times (e.g., anotherlayer stack 3-15 may be provided on top of the stack shown in FIG. 1 onthe same substrate—this applies to any and all embodiments herein).

In certain embodiments of this invention, first dielectric layer 3 maybe of or include titanium dioxide (TiO_(x) where x is from 1.7 to 2.7,most preferably 2.0 to 2.6), silicon nitride (Si_(x)N_(y) where x/y maybe about 0.75 (i.e., Si₃N₄), or alternatively x/y may be from about 0.76to 1.5 in Si-rich embodiments), silicon dioxide (SiO_(x) where x is from1.7 to 2.3, most preferably about 2.0), niobium oxide (e.g., Nb₂O₅),SiZrN, tin oxide, zinc oxide, silicon oxynitride, or any other suitabledielectric material. First dielectric layer 3 may function as anantireflection and/or color modifying layer in certain embodiments ofthis invention.

Infrared (IR) reflecting layer 9 is preferably metallic and conductive,and may be made of or include silver (Ag), gold (Au), or any othersuitable IR reflecting material. However, metallic Ag is the material ofchoice for IR reflecting layer 9 in certain example embodiments of thisinvention. The IR reflecting layer(s) helps enable the coating to havelow-E characteristics.

Barrier layers 5 and 13 are preferably at least partially oxided, and incertain embodiments of this invention are of or include nickel (Ni)oxide, or a nickel alloy oxide such as nickel chrome oxide (NiCrO_(x)),or any other suitable material(s). In the FIG. 1 embodiment, layers 5and 13 comprise NiCrO_(x) which may be either fully oxided/oxidized oronly partially oxidized. In particular, NiCrO_(x) layers 5 and 13 may befully oxidized in certain embodiments of this invention (i.e., fullystochiometric), or may be at least about 75% oxidized in otherembodiments of this invention. While NiCrO_(x) is a preferred materialfor barrier layers 5 and 13, those skilled in the art will recognizedthat other materials may instead be used (e.g., oxides of Ni, oxides ofNi alloys, oxides of Cr, oxides of Cr alloys, NiCrO_(x)N_(y), NiCrN_(x),NbO_(x) or any other suitable material) for one or more of these layers.It is noted that barrier layers 5 and 13 may or may not be continuous indifferent embodiments of this invention.

Still referring to barrier layers 5 and 13, these layers may or may notbe oxidation graded in different embodiments of this invention. In someembodiments, barrier layers 5 and 13 are approximately uniformlyoxidized throughout their respective thicknesses (i.e., no grading).However, in other embodiments, barrier layers 5 and 13 may be oxidationgraded so as to be less oxidized at the contact interface with theimmediately adjacent contact layer(s) 7, 11 than at a portion of thebarrier layer(s) further or more/most distant from the immediatelyadjacent contact layer. This may improve adhesion of the metal or metalnitride contact layers 7, 11 to the barrier layers 5, 13, respectively.Such grading may also enable the coating, in certain examplenon-limiting embodiments, to achieve the combination of heattreatability and high visible transmission. For a more detaileddiscussion of how layers 5 and/or 13 may be oxidation graded, seepending U.S. Ser. No. 09/794,224, the disclosure of which is herebyincorporated herein by reference.

Contact layers 7 and 11 (which contact IR reflecting layer 9) arepreferably more metallic and/or less oxidized than their respectiveadjacent barrier layers 5 and 13. For example, in certain embodiments ofthis invention, contact layers 7 and 11 may be of or include Ni, Cr,NiCr, CrN_(x) or NiCrN_(x) (it is noted that the term NiCrN_(x) as usedherein includes situations where the Ni in the layer is metallic and thenitriding is mostly with respect to the Cr). In such embodiments, layers7 and 11 are either not oxidized, or only slightly oxidized to an extentsignificantly less than barrier layers 5 and 13. Thus, in certainpreferred example embodiments of this invention, contact layers 7 and/or11 are substantially free of oxygen (i.e., less than about 10%oxidized), or are even oxidized from only 0-5% in certain embodiments.

Surprisingly, it has been found that by providing thin metal ormetal-nitride protective contact layers 7 and 11 (e.g., NiCr, Ni, Cr,CrN_(x), Nb, or NiCrN_(x)) on the substrate between the IR reflectinglayer 9 (e.g., Ag) and the respective barrier layers 5 and 13 (e.g.,NiCrO_(x)), durability can be improved compared to a situation whereNiCrO_(x) barrier layers 5 and 13 where entirely in direct contact withAg layer 9. The use of thin metal or metal nitride contact layers 7and/or 11 in contact with barrier layers 5 and/or 13 enables theresulting coated article to have both a high visible transmission (e.g.,at least 70% in certain example embodiments), and be durable both beforeand/or after heat treatment. It is noted that metal or metal nitridecontact layers 7 and 11 are provided to be rather thin (to reduceadverse affects of visible light absorption) in certain embodiments, sothat the contact layers 7 and 11 may or may not be continuous indifferent embodiments of this invention.

When NiCr is used in layers 5, 7, 11 and/or 13 in certain embodiments ofthis invention (i.e., when a NiCr target is used in sputtering any ofthese layers regardless of whether they are oxided, nitrided, orneither), the Ni and Cr may be provided in different amounts, such as inthe form of nichrome by weight about 80-90% Ni and 10-20% Cr. Anexemplary sputtering target for depositing these layers includes notonly SS-316 which consists essentially of 10% Ni and 90% otheringredients, mainly Fe and Cr, but Inconel and Haynes 214 alloy as well,which by weight consists essentially of (as a nominal composition) thefollowing materials which may also show up in these layers: Ni: 75.45%;Fe: 4%; Cr: 16%; C: 0.04%; Al: 4.5%; and Y:0.01%. In other embodiments,the NiCr target may be 50/50 Ni/Cr, or any other suitable ratio.

Still referring to FIG. 1, while various materials and/or thicknessesmay be used consistent with one or more of the objects discussed herein,exemplary preferred thicknesses and materials for the respective layerson the glass substrate 1 in the FIG. 1 embodiment are as follows:

TABLE 1 (Example Materials/Thicknesses; FIG. 1 Embodiment) More LayerPreferred Range (Å) Preferred (Å) Example (Å) Si_(x)N_(y) (layer 3)0-600 Å 300-500 Å 410-520 Å NiCrO_(x) (layer 5) 5-100 Å 10-50 Å 15-30 ÅNiCr (layer 7) 1-25 Å 1-10 Å 3-4 Å Ag (layer 9) 50-250 Å 80-160 Å100-140 Å NiCr (layer 11) 1-25 Å 1-10 Å 3-4 Å NiCrO_(x) (layer 13) 5-100Å 10-50 Å 15-25 Å Si_(x)N_(y) (layer 15) 0-800 Å 300-600 Å 410-540 Å

Other layer(s) below or above the illustrated coating may also beprovided. Thus, while the FIG. 1 layer system or coating is “on” or“supported by” substrate 1 (directly or indirectly), other layer(s) maybe provided therebetween. Thus, for example, the coating of FIG. 1 maybe considered “on” and “supported by” the substrate 1 even if otherlayer(s) are provided between layer 3 and substrate 1. Moreover, certainlayers of the coating may be removed in certain embodiments, whileothers may be added in other embodiments of this invention withoutdeparting from the overall spirit of certain embodiments of thisinvention.

FIG. 2 is a cross sectional view of a coated article according toanother embodiment of this invention. The FIG. 2 embodiment is the sameas the FIG. 1 embodiment, except that lower contact layer 7 from theFIG. 1 embodiment is not present in the FIG. 2 embodiment. Inparticular, a metal or metal nitride contact layer 11 is provided onlyon the upper side of Ag layer 9 because this is where the Ag layer ismost susceptible to problems arising from exposure to oxygen plasma asdiscussed above. In still further, but less preferred, embodiments ofthis invention, a metal or metal nitride contact layer may be providedon the bottom of Ag layer 9 but not on top of layer 9 (i.e., the inverseof FIG. 2). In the FIG. 2 embodiment, those skilled in the art willrecognize that layer 5 need not be NiCrO_(x), but instead may be anyother suitable material including but not limited to an oxide oftitanium (e.g., TiO₂), ZnAIO_(x), or the like.

FIG. 3 is a cross sectional view of yet another embodiment of thisinvention where metal or metal nitride contact layer(s) 7 and/or 11 canbe used. It will be appreciated by those skilled in the art that theselayers may be used in a variety of different coating stacks, anddielectric materials of the coating(s) and the number of IR reflectinglayer(s) of the coating, are not always of particular relevance withrespect to the contact layers described herein. While a metal or metalnitride contact layer (contact layer 11 over the bottom Ag layer 9, andcontact layer 11′ over the top Ag layer 9′), in other embodiments ofthis invention metal or metal nitride contact layer(s) may be providedbelow one or both of these Ag layer(s) as well (e.g., see contact layer7 in FIG. 1). In the FIG. 3 embodiment, example materials andthicknesses (which are of course non-limiting) are provided below inTable 2.

TABLE 2 (Example Materials/Thicknesses; FIG. 3 Embodiment) More LayerPreferred Range (Å) Preferred (Å) Example (Å) TiO₂ (layer 2) 0-400 Å50-250 Å 100-160 Å Si_(x)N_(y) (layer 3) 0-500 Å 50-400 Å 170-360 ÅNiCrO_(x) (layer 5) 5-100 Å 10-50 Å 15-30 Å Ag (layer 9) 50-250 Å 80-120Å 105 Å NiCr (layer 11) 1-25 Å 1-10 Å 3-4 Å NiCrO_(x) (layer 13) 5-100 Å10-50 Å 15-30 Å SnO₂ (layer 16) 0-800 Å 500-850 Å 650 Å Si_(x)N_(y)(layer 18) 0-800 Å 50-250 Å 170 Å NiCrO_(x) (layer 5′) 5-100 Å 10-50 Å15-30 Å Ag (layer 9′) 50-250 Å 80-120 Å 105 Å NiCr (layer 11′) 1-25 Å1-10 Å 3-4 Å NiCrO_(x) (layer 13′) 5-100 Å 10-50 Å 15-30 Å SnO₂ (layer20) 0-500 Å 100-300 Å 150 Å Si₃N₄ (layer 22) 0-500 Å 100-300 Å 250 Å

An example of the FIG. 1 embodiment of the instant invention was madeand tested, as set forth below. During the sputter coating process inwhich layers 3-15 were deposited: the line speed for lower siliconnitride layer 3 (using a Si sputtering target) was 55 inches/minuteusing 8 passes, the line speed for upper silicon nitride layer 15 (usinga Si sputtering target) was 50 inches/minute using 8 passes; the linespeed for the NiCr contact layers 7 and 11 was 100 inches/minute using 1pass; and the line speed for the NiCrO_(x) barrier layers 5 and 13 was37.5 inches/minute using 2 passes.

COATER SET-UP FOR EXAMPLE OF FIG. 1 EMBODIMENT

Target Power Volts Ar O₂ N₂ Thick- Mat'l (kW) (V) (sccm) (sccm) (sccm)ness (Å) Si (layer 1 kW 485 V 40 0 40 470 Å 3) NiCr 1 kW 415 V 40 10 0 22 Å (layer 5) NiCr 0.38 kW 370 V 30 0 0  3 Å (layer 7) Ag 2.95 kW 465V 30 0 0 R_(s) = 16 (layer 9) ohm/sq. NiCr 0.38 kW 370 V 30 0 0  3 Å(layer 11) NiCr 1 kW 415 V 40 10 0  22 Å (layer 13) Si 1 kW 485 V 40 040 510 Å (layer 15)

As will be appreciated by those skilled in the art, the aforesaid coaterset-up resulted in a layer stack on glass substrate 1 of (from thesubstrate outwardly): Si₃N₄/NiCrO_(x)NiCr/Ag/NiCr/NiCrO_(x)/Si₃N₄. Ofcourse, in alternative embodiments of this invention contact layer(s) 7and/or 11 could be nitrided (fully or only partially) by adding nitrogengas to the sputter coating process of those layers 7 and/or 11. Opticalcharacteristics of this particular example were measure as follows (Ill.C, 2 degree observer technique was used for transmissioncharacteristics):

OPTICAL CHARACTERISTICS OF EXAMPLE

Transmission (TY) %: 81.25% a*_(T): −2.24 b*_(T): 0.81 Reflectance asviewed from 7.54 glass (G) side: R_(G)Y (%): L*_(G): 33.01 a*_(G): 0.56b*_(G): −7.13 Reflectance as viewed from 5.07 film/coating (F) side:R_(F)Y (%): a*_(F): 3.21 b*_(F): −5.30 R_(S) (sheet resistance inohms/sq.): 16.0

This example was characterized by better durability than a comparativeexample where the metal contact layers were omitted.

Coated articles according to certain embodiments of this invention havea visible transmission of at least 65%, more preferably of at least 70%,and most preferably of at least 75%, and even sometimes at least 80%.Moreover, coated articles according to certain example embodiments ofthis invention have a sheet resistance (R_(S)) of no greater than 20ohms/sq., more preferably no greater than 16 ohms/sq., and sometimes nogreater than 12 ohms/sq.

While the invention has been described in connection with what ispresently considered to be the most practical and preferred embodiment,it is to be understood that the invention is not to be limited to thedisclosed embodiment, but on the contrary, is intended to cover variousmodifications and equivalent arrangements included within the spirit andscope of the appended claims.

What is claimed is:
 1. A heat treated coated article comprising: a glasssubstrate; a coating supported by the glass substrate, wherein thecoating comprises a first dielectric layer, an Ag inclusive layer, alayer comprising an oxide of NiCr, and a second dielectric layer,wherein the Ag inclusive layer is located between the first dielectriclayer and the layer which comprise an oxide of NiCr; and wherein thecoating further includes a metal or metal nitride contact layer locateddirectly between and contacting each of the Ag inclusive layer and thelayer comprising an oxide of NiCr, wherein said metal or metal nitridecontact layer is more metallic than said adjacent layer comprising anoxide of NiCr.
 2. The coated article of claim 1, wherein the contactlayer is on an upper side of the Ag inclusive layer, and is metallic andconsists essentially of nickel.
 3. The coated article of claim 1,wherein the layer comprising an oxide of NiCr is located directlybetween and contacting each of a layer comprising silicon nitride andsaid contact layer.
 4. The coated article of claim 1, wherein thecontact layer comprises a nitride of NiCr and is less oxidized than saidlayer comprising an oxide or NiCr that the contact layer is in contactwith.
 5. The coated article of claim 1, wherein the layer comprising anoxide of NiCr is more metallic at a location closer to the silverinclusive layer than at another location further from the silverinclusive layer.
 6. The coated article of claim 1, wherein the metal ormetal nitride contact layer comprises at least one of Ni and a nitrideof NiCr.
 7. The coated article of claim 1, wherein the coated articlehas a visible transmission of at least 70%.
 8. The coated article ofclaim 7, wherein the coated article has a visible transmission of atleast 75%.
 9. The coated article of claim 1, where the coating has asheet resistance (R_(S)) of no greater than 20 ohms/sq.
 10. The coatedarticle of claim 1, wherein the first dielectric layer comprises siliconnitride.
 11. The coated article of claim 10, wherein the seconddielectric layer comprises silicon nitride.
 12. The coated article ofclaim 1, wherein the first dielectric layer comprises an oxide oftitanium.
 13. The coated article of claim 1, wherein the contact layeris provided on the upper surface of the Ag inclusive layer.
 14. A heattreated coated article including a coating supported by a substrate, thecoating comprising: a layer comprising an oxide of NiCr; an Ag inclusivelayer; and a metal or metal nitride layer located between and contactingeach of the layer comprising an oxide of NiCr and the Ag inclusivelayer, wherein the metal or metal nitride layer is more metallic than isthe layer comprising an oxide of NiCr.
 15. The coated article of claim14, wherein the layer comprising an oxide of NiCr is oxidation graded soas to be more metallic at a location closer to the metal or metalnitride layer than at a location further from the metal or metal nitridelayer.
 16. The coated article of claim 14, wherein the metal or metalnitride layer is of at least one of Ni, a nitride of Cr, and a nitrideof NiCr.
 17. The coated article of claim 14, wherein the coating has asheet resistance (R_(S)) of no greater than 20 ohms/sq.
 18. A heattreated coated article including a coating supported by a substrate, thecoating comprising: an oxide layer including an oxide of a metal ormetal alloy; an infrared (IR) reflecting layer; a metal or metal nitridecontact layer located between and contacting each of the IR reflectinglayer and the oxide layer; wherein the oxide layer is more metallic at alocation closer to the metal or metal nitride contact layer than atanother location further from the metal or metal nitride contact layer;and wherein the metal or metal nitride contact layer comprises at leastone metal which is also in the oxide layer.
 19. The coated article ofclaim 18, wherein the oxide layer comprises an oxide of NiCr, andwherein the metal or metal nitride contact layer comprises Ni so thatsaid at least one metal that the contact layer and the oxide layer havein common comprises Ni.
 20. The coated article of claim 19, wherein theIR reflecting layer comprises Ag.
 21. The coated article of claim 18,wherein the metal or metal nitride contact layer is metallic and is ofNi, and is located on an upper side of the IR reflecting layer, andwherein the IR reflecting layer comprises Ag.
 22. The coated article ofclaim 18, wherein the coated article is characterized by a sheetresistance (R_(S)) of no greater than 20 ohms/sq., and a visibletransmission of at least 70%.
 23. The coated article of claim 1, whereinthe metal or metal nitride contact layer is of a lesser thickness thanthe layer comprising an oxide of NiCr.
 24. The coated article of claim1, wherein the metal or metal nitride contact layer is from about 1-10 Åthick, and the layer comprising an oxide of NiCr is from about 10-50 Åthick.
 25. The coated article of claim 14, wherein the metal or metalnitride layer is from about 1-10 Å thick, and the layer comprising anoxide of NiCr is from about 10-50 Å thick.
 26. The coated article ofclaim 18, wherein the metal or metal nitride contact layer is from about1-10 Å thick, and the oxide layer which contacts the metal or metalnitride contact layer is from about 10-50 Å thick.
 27. The coatedarticle of claim 1, wherein the contact layer is substantially free ofoxygen.
 28. The coated article of claim 14, wherein the metal or metalnitride layer is oxidized from 0-5%.
 29. The coated article of claim 14,wherein the contact layer has at least one metal in common with thelayer comprising an oxide of NiCr which is in a contact with the contactlayer.
 30. The coated article of claim 14, wherein the metal or metalnitride layer has at least one metal in common with the layer comprisingan oxide of NiCr which is in contact with the metal or metal nitridelayer.
 31. A heat treated coated article comprising: a glass substrate;a coating supported by the glass substrate, wherein the coatingcomprises a first dielectric layer, an Ag inclusive layer, a layercomprising an oxide of NiCr, and a second dielectric layer, wherein theAg inclusive layer is located between the first dielectric layer and thelayer comprising an oxide of NiCr; wherein the coating further includesa contact layer comprising a metal located between and contacting the Aginclusive layer and the layer comprising an oxide of NiCr; and whereinthe layer comprising an oxide of NiCr is oxidation graded so as to bemore metallic at a location closer to the contact layer than at anotherlocation further from the contact layer.
 32. The coated article of claim31, wherein the contact layer is metallic and is of Ni.
 33. The coatedarticle of claim 31, wherein the contact layer is more metallic and lessoxidized than is the layer comprising an oxide of NiCr.